武汉理工大学学报 ›› 1999, Vol. 21 ›› Issue (3) : 21-23.
论文

利用高钙粉煤灰生产粉煤灰水泥的试验研究

  • 张世贤
作者信息 +
History +

摘要

研究了高钙粉煤灰水泥的细度及活性激发剂对其物理性能的影响。研究结果表明,高钙粉煤灰水泥的安定性和各龄期的抗折、抗压强度均随着水泥的细度的提高和活性激发剂的掺入而提高,活性激发剂具有加速水泥矿物和f Ca O 水化的作用。采用525# 熟料,掺加30% 的高钙粉煤灰时,水泥的比表面积在340~400 m 2 /kg 和掺入1% 的活性激发剂,能够稳定生产425# 高钙粉煤灰水泥。

Abstract

Experimental Research of Using High Calcium Fly Ash Produced Fly Ash Cement Zhang Shixian Zhou Tao Wang ZhiquanStudied the influence of the fineness of the cement with high calcium fly ash and active agent on the physical properties. The results showed that the flexible and compressive strengths at different ages and stability of the cement with high calcium fly ash increased with the increasing of cement fineness and the adding of active agent, which accelerated the hydration of the cement minerals and f CaO. By using 525 # clinker, in the case that adding 30% high calcium fly ash and 1% active agent, 425 # high calcium fly ash cement with 340~400 m\+2/kg specific surface area can be stably produced.high calcium fly ash; fineness; stability; active agent

引用本文

导出引用
张世贤. 利用高钙粉煤灰生产粉煤灰水泥的试验研究. 武汉理工大学学报. 1999, 21(3): 21-23

参考文献

PDF(229 KB)

67

Accesses

0

Citation

Detail

段落导航
相关文章

/